PROPERTIES AND MORPHOLOGICAL OF MORTAR CONTAINING USED ENGINE OIL
DOI:
https://doi.org/10.22441/ijimeam.v4i1.15132Keywords:
Used Engine Oil, Mortar, Retarder, EttringiteAbstract
Engine oil has an important role in the design and operation of all automotive engines. Used engine oil is a waste product produced in high quantity in the workshop garage which commonly found in most cities in Indonesia. The utilization of used engine oil has shown potential as retarder by reduce the setting time of mortar. In this study mortar was made by mixing cement,light aggregate, water, and engine oil both new and used as admixture ranged 0-1%. Mortar sample treatment is carried out at room temperature. The samples were tested for setting time and compressive strength after 3, 7 and 28 days curing. Scanning Electron Microscope characterization was carried out to to find out the morphological structure of resulting mortar. Results shown that the mortar with the addition of 0.75% used engine oil has the highest compressive test result of 9.31 MPa when the mortar reached 28 days compared to mortar without engine oil addition has a compressive test result of 7.546 MPa. SEM Images shown there are more ettringite presents in mortar with used engine oil addition.Downloads
References
Briffa, J. Sinagra, E. & Blundell, R. Heavy metal pollution in the environment and their toxicological effects on humans. Heliyon 2020; 6(9);e04691.
S A Ratiu et al . IOP Conf. Ser.: Mater. Sci. Eng. 2022;1220;012034
Carolina T. Pinheiro, Margarida J. Quina & Licínio M. Gando-Ferreira. Management of waste lubricant oil in Europe: A circular economy approach, Critical Reviews in Environmental Science and Technology, 2021;51:18, 2015-2050.
Osman, D.I. Attia, S.K. & Taman, A.R. Recycling of used engine oil by different solvent. Egyptian Journal of Petroleum. 2018; 27(2); 221-225.
Sánchez-Alvarracín, C. Criollo-Bravo, J. Albuja-Arias, D. García-Ávila, F. & Pelaez-Samaniego, MR. Characterization of Used Lubricant Oil in a Latin-American Medium-Size City and Analysis of Options for Its Regeneration. Recycling. 2021; 6(1):10
Nowak P, Kucharska K, Kamiński M. Ecological and Health Effects of Lubricant Oils Emitted into the Environment. Int J Environ Res Public Health. 2019;16(16):3002.
Ali, H. Khan, E. & Ilahi, I. Environmental Chemistry and Ecotoxicology of Hazardous Heavy Metals: Environmental Persistence, Toxicity, and Bioaccumulation. Journal of Chemistry. 2019.
Boadu et al. A Review of Methods for Removal of Contaminants in Used Lubricating Oil. CSIJ 2019. 26(4);1-11
Adewole, B.Z. Olojede, J.O. Owolabi, H.A. & Obisesan, O.R. Characterization and Suitability of Reclaimed Automotive Lubricating Oils Reprocessed by Solvent Extraction Technology. Recycling. 2019; 4(3):31
Ugwele, F.O. Aninwede, C.S. Chime, T.O. Christian, O.A. Innocent, S.I. Application of response surface methodology in optimizing the process conditions for the regeneration of used mobil oil using different kinds of acids. Heliyon. 2020;6(10):e05062.
ASTM C191, Standard Test Method for Time of Setting of Hydraulic Cement by Vicat Needle, ASTM International. 2021.
ASTM C109, Standard Test Method for Time of Setting of Hydraulic Cement by Vicat Needle, ASTM International. 2021.
Huang, H. Yuan, Q. Deng, D. Peng, J. & Huang Y. Effects of chemical and mineral admixtures on the foam indexes of cement-based materials. Case Studies in Construction Materials 2019;11;e00232.
García-Vera, V.E. Tenza-Abril, A.J. Saval, J.M. Lanzón, M. Influence of Crystalline Admixtures on the Short-Term Behaviour of Mortars Exposed to Sulphuric Acid. Materials. 2019; 12(1):82
Barbhuiya, S. & Kumala, D. Behaviour of a Sustainable Concrete in Acidic Environment. Sustainability. 2017; 9(9):1556.
Rahman, T. Djamal, M. Nurdiana, J. & Ghulam, A.M. The Effect of Plastocrete® RT6 Plus and Coca-Cola Admixtures on The Concrete Setting Time and Strength. Preprints 2020, 2020010094
K. Poongodi et al. IOP Conf. Ser.: Mater. Sci. Eng 2019. 561 012067
Kunther, W. Ferreiro, S. & Skibsted. Influence of the Ca/Si ratio on the compressive strength of cementitious calcium–silicate–hydrate binders. J. J. Mater. Chem. A, 2017,5, 17401-17412.
Wang, S. Peng, X. Tang, L. Cao, C. Zeng, L. Contact-Hardening Behavior of Calcium Silicate Hydrate Powders. Materials (Basel). 2018;11(12):2367. Published 2018 Nov 25. doi:10.3390/ma11122367
Shaohong Zhu et al. Preparation of nano-calcium silicate hydrate and its application in concrete. IOP Conf. Ser.: Mater. Sci. Eng 2019. 631 022052
Downloads
Published
How to Cite
Issue
Section
License
Authors who publish in IJIMEAM retain the following rights:- Author retains the copyright and grants the journal the right of first publication of the work simultaneously licensed under the Creative Commons Attribution-ShareAlike 4.0 License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Author is able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book) with the acknowledgment of its initial publication in this journal.
- Author is permitted and encouraged to post his/her work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of the published work (See What is Open Access).
Read more about the Creative Commons Attribution-ShareAlike 4.0 Licence here: https://creativecommons.org/licenses/by-sa/4.0/.